Enhanced bulk modulus and reduced transition pressure in γ- nanocrystals
Department of Physics, Building 307, Technical University of Denmark, DK-2800 Lyngby, Denmark
2 Niels Bohr Institute, Oersted Laboratory - DK-2100 Copenhagen, Denmark
Accepted: 15 October 1998
Synchrotron radiation X-ray diffraction studies of γ- have been performed with emphasis on the pressure-induced phase transformation and the equation of state of the nanophase material. For γ- the bulk modulus has been found to increase from 203 GPa for the bulk material to 305 GPa for 9 nm size crystals. At the same time the transition pressure decreases from 35 to 27 GPa. The reduced transition pressure is explained in terms of nucleation and growth, the larger volume change upon transition in the nanocrystalline material being the main factor.